A-Tech 1110 Super High Impact Polystyrene

Combination of Cost Reduction, High Impact and High Gloss Properties

| Characteristic & Application | Data Sheet | Comparison with HIPS and ABS | Dart Impact Test Result | Gloss Performance | Contact Us |

A-Tech 1110 super high impact polystyrene resin is a glossy, high-impact resin with a processing and cost advantage for injection-molding applications such as toys and small appliances.

¡@

A-Tech1110 bridges the gap between ABS & HIPS


¡@

Characteristic:

  • Cost Advantage
    • Lower material price, 8-10% compare to ABS
    • Electric cost, No need pre-drying
    • Coloring, consistent white-base color leads easy coloring and correction time reduction
    • Lower density (A-Tech 1110 ~ 1.05g/cm3 vs. ABS ~ 1.07g/cm3), consumes less plastic materials
      ¡@
  • Excellent impact resistant properties, close to ABS
  • Glossy outlook 70%-80% of ABS
  • Easy processing with short cycle time and High flow rate
  • Heat resistance 
  • Comply to International Safety Standard (e.g. FDA, RoHs, EN71, UL)
  • FDA compliant
  • Production in Hong Kong (3-4days)
¡@
Application: 
  • Small appliance
  • Toys
  • Premiums
  • Printers
  • Remote controls





¡@

 Back to Top

Table 1: A-Tech 1110 Data Sheet
Properties  Test Method  Test Unit  Test Value
Notched Izod @23 ¢XC  ASTM D 3029  kg-cm/cm  24.5
Melt Flow Rate  ASTM D 1238  g/10min  3
Flexural Strength  ASTM D 790  kg/cm2  458
Tensile Strength  ASTM D 638  kg/cm2  197
Deflection Temp. Under Load
@ 1.82MPa, Annealed		 ASTM D 648 ¢XC 99
Vicat Softening Point  ASTM D 1525  ¢XC 102
UL94 Classification @ 1.5mm ¡@ ¡@  ¡@ ¡@ HB
FDA ¡@ ¡@  ¡@ ¡@

FDA compliant

The data is intended as a general guide only. We make no guarantee of results and assume no obligation or liability.

 Back to Top

Table 2: Comparison of physical properties between HIPS, A-Tech and ABS
¡@ ¡@ ¡@ A-Tech (SHIP) ABS HIPS
Properties   Test Method  Test Unit   A-Tech 1110 ¡@ ¡@
Notched Izod @23 ¢XC ASTM D 3029  kg-cm/cm   24.5  20 11
Flexural Strength  ASTM D 790  kg/cm2  458 790 360 
Deflection Temp. Under Load
@ 1.82MPa, Annealed		 ASTM D 648 ¢XC 99 99 99
Vicat Softening Point  ASTM D 1525  ¢XC 102 97 90 
FDA ¡@ ¡@  ¡@ ¡@ FDA compliant  FDA compliant  FDA compliant 
UL94 Classification @1.5mm ¡@ ¡@ HB HB  HB
The data is intended as a general guide only. We make no guarantee of results and assume no obligation or liability. 

 Back to Top

Photo 1: Result of instrument dart impact test (ASTM D 3763)

 Back to Top

Graph 2: The gloss as function of mold temperature (ASTM D 532)

 Back to Top

Contact Person: Mr. Anson Liu (Direct line: 852-2687-7126)
Marketing Executive
Ngai Hing Hong Plastic Materials (Hong Kong) Ltd.
Email:  nh.anson.liu@nhh.com.hk
Fax: 852-2694-0877

 Back to Top